Dibolutu tša Hex tša Oxide tše Ntsho .
Maemo: DIN 960 .
Mofuta wa khoele: khoele e ntle, karolo ya khoele .
Setšweletšwa: Dibolutu tša Hex tša Oxide ye Ntsho .
Gape e reeletšwe ka: Black Hex Bolts .
Thepa: Tšepe ea khabone .
Sehlopha sa thepa: 5.6, 8.8, 10.9.
Bophara: M8 × 1, m10 × 1, m10 × 1,25, m12 × 1,25, m12 × 1,5, (M14 × 1,5 × 1,5, (M18 × 20 × 1,5, m20 × 2, (M22 × 1.5), (M22 × 2 24, m24, m24, m24, m24, m24, m24, m24, m24, m24, m24, m24, m24, m24, m24, m24, m24, m24, m24, m24, m24, m24, m24, m24, m24, m24, m24, m24, m24, m24, m24, M2 m30 × 2, (m33 × 2), m36 × 3, (m39 × 3), m42 × 3, (m45 × 3 , m48 × 3, (m52 × 4), m56 × 4, (m60 × 4), m64 × 4, (m68 × 4), m72 × 4, m76 × 4), (m80 × 4), m80 × 4), m80 × 4), m80 × 4), m80 × 4), m80 × 4), m80 × 4), m80 × 4 000 000 000 000 000 000 000 000 000 000 000 000 000 000 000 000 000 000 000 000 000 000 000 000).
qeta: thota, e ntšo oxide, zinki plated, chesang ina galvanized, oxidation, dacromet, phosphating, cadmium electroplate, nikele plated
Mohuta wa Hlogo: Hlogo ya Hexagon .
Mofuta wa drive: hex ya ka ntle .
MOQ: 1000kgs ya 1000kg .
Nako ya go eta pele: matšatši a 30 go ya go a 60 .
Matseno a Setšweletšwa .
Aya Fasteners (Hebei) Co., Ltd. ke e mong oa bahlahisi ba nang le phihlelo ka ho fetisisa le bafepedi ba Black Oxide Hex Bolts ka China. Hle ikwe o lokologile go reka dibolutu tša boleng bja godimo tša Black Oxide Hex tšeo di dirilwego ka China mo go tšwa feketoring ya rena. Bakeng sa therišano ya theko, ikgokaganye le rena.

Bjalo ka moabi wa lefase ka bophara wa ditharollo tša go kgomaretša tše di rulagantšwego, tshepedišo ya tirelo ya Aya le yona e kgauswi le bareki go swana le ditšweletšwa tša Aya. Go tšwa go go hlaloša dinyakwa tša go latela-Ditirelo tša godimo, AYA e tla se bane maiteko a go thuša bareki go rarolla mathata afe goba afe a go kgomaretša ao a tšwelelago, go fediša go tshwenyega ga bareki.
Tlhaloso ya Setšweletšwa .
Lebitso la sehlahiswa . | Dibolutu tša Hex tša Oxide tše Ntsho . |
Gape o reeletšwe ka maina . | Dibolutu tša Hex tše Ntsho . |
Didirišwa | Tšepe ya khabone . |
Motheo | DIN 960 . |
Sehlopha sa thepa . | 5.6, 8.8, 10.9 |
Bophara ba . | M8×1, M10×1, M10×1.25, M12×1.25, M12×1.5, (M14×1.5), M18×1.5, (M18×2), M20×1.5, M20×2, (M22×1.5), (M22×2), M24×1.5, M24×2, (M27×2), M30×2, (M33×2), M36×3, (M39×3), M42×3, (M45×3), M48×3, (M52×4), M56×4, (M60×4), M64×4, (M68×4), M72×4, (M76×4), (M80×4), M100×4 |
Fetša | thota, oxide e ntšo, zinki plated, chesang ina galvanized, oxidation, dacromet, phosphating, cadmium electroplate, nikele plated |
Mohuta wa Hlogo . | Hlogo ya Hexagon . |
Mofuta wa drive . | Hex ya ka ntle . |
Mohuta wa khoele . | khoele e ntle, khoele e sa fellang . |
Tafole ya Ditekanyo .

| Khoele ya sekurufu . | M8 | M10 | M12 | (M14) | M16 | (M18) | M20 | (M22) | M24 | (M27) | M30 | (M33) | M36 | (M39) | |||
| d | |||||||||||||||||
| P | Segalo | Thread e ntle-1. | 1 | 1 | 1.5 | 1.5 | 1.5 | 2 | 1.5 | 2 | 2 | 2 | 2 | 2 | 3 | 3 | |
| Khoele e ntle-2. | - | 1.25 | 1.25 | - | - | 1.5 | 2 | 1.5 | 1.5 | - | - | - | - | - | |||
| b | l ka fase ga goba go lekana le 125 . | 22 | 26 | 30 | 34 | 38 | 42 | 46 | 50 | 54 | 60 | 66 | 72 | 78 | 84 | ||
| 125 l ka fase ga goba go lekana le 200 . | 28 | 32 | 36 | 40 | 44 | 48 | 52 | 56 | 60 | 66 | 72 | 78 | 84 | 90 | |||
| L>200 | 41 | 45 | 49 | 53 | 57 | 61 | 65 | 69 | 73 | 79 | 85 | 91 | 97 | 103 | |||
| c | Min . | 0.15 | 0.15 | 0.15 | 0.15 | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | 0.3 | ||
| Max . | 0.6 | 0.6 | 0.6 | 0.6 | 0.8 | 0.8 | 0.8 | 0.8 | 0.8 | 0.8 | 0.8 | 0.8 | 0.8 | 1 | |||
| da | Max . | 9.2 | 11.2 | 13.7 | 15.7 | 17.7 | 20.2 | 22.4 | 24.4 | 26.4 | 30.4 | 33.4 | 36.4 | 39.4 | 42.4 | ||
| ds | Max . | 8 | 10 | 12 | 14 | 16 | 18 | 20 | 22 | 24 | 27 | 30 | 33 | 36 | 39 | ||
| mphato wa A . | Min . | 7.78 | 9.78 | 11.73 | 13.73 | 15.73 | 17.73 | 19.67 | 21.67 | 23.67 | - | - | - | - | - | ||
| Mphato wa B . | Min . | 7.64 | 9.64 | 11.57 | 13.57 | 15.57 | 17.57 | 19.48 | 21.48 | 23.48 | 26.48 | 29.48 | 32.38 | 35.38 | 38.38 | ||
| dw | mphato wa A . | Min . | 11.6 | 15.6 | 17.4 | 20.5 | 22.5 | 25.3 | 28.2 | 30 | 33.6 | - | - | - | - | - | |
| Mphato wa B . | Min . | 11.4 | 15.4 | 17.2 | 20.1 | 22 | 24.8 | 27.7 | 29.5 | 33.2 | 38 | 42.7 | 46.6 | 51.1 | 55.9 | ||
| e | mphato wa A . | Min . | 14.38 | 18.9 | 21.1 | 24.49 | 26.75 | 30.14 | 33.53 | 35.72 | 39.98 | - | - | - | - | - | |
| Mphato wa B . | Min . | 14.2 | 18.72 | 20.88 | 23.91 | 26.17 | 29.56 | 32.95 | 35.03 | 39.55 | 45.2 | 50.85 | 55.37 | 60.79 | 66.44 | ||
| k | Bogolo bja leina . | 5.3 | 6.4 | 7.5 | 8.8 | 10 | 11.5 | 12.5 | 14 | 15 | 17 | 18.7 | 21 | 22.5 | 25 | ||
| mphato wa A . | Min . | 5.15 | 6.22 | 7.32 | 8.62 | 9.82 | 11.28 | 12.28 | 13.78 | 14.78 | - | - | - | - | - | ||
| Max . | 5.45 | 6.58 | 7.68 | 8.98 | 10.18 | 11.72 | 12.72 | 14.22 | 15.22 | - | - | - | - | - | |||
| Mphato wa B . | Min . | 5.06 | 6.11 | 7.21 | 8.51 | 9.71 | 11.15 | 12.15 | 13.65 | 14.65 | 16.65 | 18.28 | 20.58 | 22.08 | 24.58 | ||
| Max . | 5.54 | 6.69 | 7.79 | 9.09 | 10.29 | 11.85 | 12.85 | 14.35 | 15.35 | 17.35 | 19.12 | 21.42 | 22.92 | 25.42 | |||
| k1 | Min . | 3.54 | 4.28 | 5.05 | 5.96 | 6.8 | 7.8 | 8.5 | 9.6 | 10.3 | 11.7 | 12.8 | 14.4 | 15.5 | 17.2 | ||
| r | Min . | 0.4 | 0.4 | 0.6 | 0.6 | 0.6 | 0.6 | 0.8 | 0.8 | 0.8 | 1 | 1 | 1 | 1 | 1 | ||
| s | Max=bogolo bja leina . | 13 | 17 | 19 | 22 | 24 | 27 | 30 | 32 | 36 | 41 | 46 | 50 | 55 | 60 | ||
| mphato wa A . | Min . | 12.73 | 16.73 | 18.67 | 21.67 | 23.67 | 26.67 | 29.67 | 31.61 | 35.38 | - | - | - | - | - | ||
| Mphato wa B . | Min . | 12.57 | 16.57 | 18.48 | 21.16 | 23.16 | 26.16 | 29.16 | 31 | 35 | 40 | 45 | 49 | 53.8 | 58.8 | ||
| Khoele ya sekurufu . | M42 | (M45) | M48 | (M52) | M56 | (M60) | M64 | (M68) | M72 | (M76) | M80 | M90 | M100 | |||
| d | ||||||||||||||||
| P | Segalo | Thread e ntle-1. | 3 | 3 | 3 | 3 | 4 | 4 | 4 | 4 | 4 | 4 | 4 | 4 | 4 | |
| Khoele e ntle-2. | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
| b | l ka fase ga goba go lekana le 125 . | 90 | 96 | 102 | - | - | - | - | - | - | - | - | - | - | ||
| 125 l ka fase ga goba go lekana le 200 . | 96 | 102 | 108 | 116 | 124 | 132 | 140 | 148 | 158 | 164 | 172 | 192 | - | |||
| L>200 | 109 | 115 | 121 | 129 | 137 | 145 | 153 | 161 | 169 | 177 | 185 | 205 | 225 | |||
| c | Min . | 0.3 | 0.3 | 0.3 | 0.3 | - | - | - | - | - | - | - | - | - | ||
| Max . | 1 | 1 | 1 | 1 | 1 | 1 | 1 | 1 | 1 | 1 | 2 | 2 | 2 | |||
| da | Max . | 45.6 | 48.6 | 52.6 | 56.6 | 63 | 67 | 71 | 75 | 79 | 83 | 87 | 97 | 108 | ||
| ds | Max . | 42 | 45 | 48 | 52 | 56 | 60 | 64 | 68 | 72 | 76 | 80 | 90 | 100 | ||
| mphato wa A . | Min . | - | - | - | - | - | - | - | - | - | - | - | - | - | ||
| Mphato wa B . | Min . | 41.38 | 44.38 | 47.38 | 51.26 | 55.26 | 59.26 | 63.26 | 67.26 | 71.26 | 75.26 | 79.26 | 89.13 | 99.13 | ||
| dw | mphato wa A . | Min . | - | - | - | - | - | - | - | - | - | - | - | - | - | |
| Mphato wa B . | Min . | 59.9 | 64.7 | 69.4 | 74.2 | 78.7 | 83.4 | 88.2 | 92.9 | 97.7 | 102.4 | 107.2 | 121.1 | 135.4 | ||
| e | mphato wa A . | Min . | - | - | - | - | - | - | - | - | - | - | - | - | - | |
| Mphato wa B . | Min . | 71.3 | 76.95 | 82.6 | 88.25 | 93.56 | 99.21 | 104.86 | 110.51 | 116.16 | 121.81 | 127.46 | 144.08 | 161.03 | ||
| k | Bogolo bja leina . | 26 | 28 | 30 | 33 | 35 | 38 | 40 | 43 | 45 | 48 | 50 | 57 | 63 | ||
| mphato wa A . | Min . | - | - | - | - | - | - | - | - | - | - | - | - | - | ||
| Max . | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
| Mphato wa B . | Min . | 25.58 | 27.58 | 29.58 | 32.5 | 34.5 | 37.5 | 39.5 | 42.5 | 44.5 | 47.5 | 49.5 | 56.4 | 62.4 | ||
| Max . | 26.42 | 28.42 | 30.42 | 33.5 | 35.5 | 38.5 | 40.5 | 43.5 | 45.5 | 48.5 | 50.5 | 57.6 | 63.6 | |||
| k1 | Min . | 17.9 | 19.3 | 20.9 | 22.8 | 24.2 | 26.2 | 27.6 | 29.8 | 31.2 | 33.2 | 34.6 | 39.5 | 43.7 | ||
| r | Min . | 1.2 | 1.2 | 1.6 | 1.6 | 2 | 2 | 2 | 2 | 2 | 2 | 2 | 2.5 | 2.5 | ||
| s | Max=bogolo bja leina . | 65 | 70 | 75 | 80 | 85 | 90 | 95 | 100 | 105 | 110 | 115 | 130 | 145 | ||
| mphato wa A . | Min . | - | - | - | - | - | - | - | - | - | - | - | - | - | ||
| Mphato wa B . | Min . | 63.1 | 68.1 | 73.1 | 78.1 | 82.8 | 87.8 | 92.8 | 97.8 | 102.8 | 107.8 | 112.8 | 127.5 | 142.5 | ||
Dintlha tša Setšweletšwa .

Melemo ya sehlahiswa .

Melemo ya dibolutu tsa hex e ntšo .
1. Black Oxide Hex Bolts e na le ditshenyagalelo tše di amogelegago go feta dibolutu tše dingwe tšeo di nago le dikalafo tša go hlohleletša.
2. Hlogo ya Hex e dira gore go be bonolo go tsenya le go diriša mehuta ya ditikologo tša mošomo.
3. E na le ponagalo ya moswananoši ge e bapetšwa le mohuta wo mongwe wa galvanizing go swana le ditikologo tša go šomiša.
4. E na le bophelo ba tšebeletso e makatsang ka lebaka la le rona thata RAW thepa tlhahlobo tsamaiso le QC sehlopha.
5. Aya o na le 24/7 ka morago ga-thekišo sehlopha go thuša ka wena mohuta wa ditaba ka morago ga go fihla gabotse, go tšwa go installment go ya go didirišwa.
6. Aya o na le maitemogelo a mengwaga ye e fetago ye 10 a go romela ntle kgwebo go go thuša go šomana le mehuta ya mathata.
Tlhahlobo ya Boleng .

Go phuthela & go rwala setshelo .

Maemo a Tšhomišo .

Ke ka baka la’ng o kgetha Aya?

Dithegi tše di fišago .: Black oxide hex bolts, China, bafepedi, bahlahisi, fektheri, reka, theko, bakeng sa thekiso, entsoeng ka China